用于润滑油改性的乙丙共聚物的合成

蔡小平　邹向阳　张红江　廖凤英　谢妤

　　摘要：以V-A1体系为催化剂，己烷为溶剂，采用分子量调节剂合成出了组 成、结构、分子量及分子量分布与美国Exxon-8921基本相同的润滑油改性用乙丙共聚物。 经应用评定证明其综合性能好，适合调制各种中、高档多级内燃机油，并在2万t /aEPDM生产装置上实现工业化。
　　关键词：润滑油；乙丙共聚物；合成
　　中图分类号：TQ333.4　　文献标识码：A　　文章编号：1005-3174(2000)03-0001-04

Synthesis of ethylene propylene copolymer used as
viscosity index improver for lubricating oil

CAI Xiao-ping,ZOU Xiang-yang,ZHANG Hong-jiang,LIAO Feng-ying,XIE Yu
（Research Institute of Jilin Petrochemical Company,PetroCh ina Company Limited,Jilin 132021,China）

ABSTRACT

　　Ethylene propylene copolymer used as viscosity index improver for lubri cating oil was synthesized by using V-Al as catalyst,hexane as solvent and ETCA as molecular weight adjusting agent,the product is almost the same as that of E xxon-8921 in composition,micro structure,molecular weight and molecular weight d istribution.It has been indicated by applying examinations that the product has excellent comprehensive properties and is suited for making virous degrades of multisage internal combustion engine oils.The technology based on which has bee n used in the 20,000t/a EPDM commercial plant.
　　Key words:lubricating oil;ethylene propylene copolymer;syn thesis

基金项目：中国石油天然气集团公司资助项目(990806-11)
作者简介：蔡小平(1964—)，男，湖南省宁远县人，博士，高 级工程师，多年从事稀土金属有机化合物的合成及催化双烯烃聚合反应的研究。先后两次在 德国马丁—路德大学(1994～1995)和英国萨塞克斯大学(1998～1999)就该领域开展国际合 作研究 。现主要从事高分子溶液聚合的研究开发，三项成果通过省级鉴定，在国内外学术刊物发 表论文数十篇。
蔡小平（中国石油吉林石化公司研究院，吉林吉林　132021）
邹向阳（中国石油吉林石化公司研究院，吉林吉林　132021）
张红江（中国石油吉林石化公司研究院，吉林吉林　132021）
廖凤英（中国石油吉林石化公司研究院，吉林吉林　132021）
谢妤（中国石油吉林石化公司研究院，吉林吉林　132021）

参考文献：
［1］　朱倜夫.作粘度指数改进剂的乙丙共聚物的合成［J］.合成橡胶工业 ，1982，5(1)，12-14.
［2］　长春应化所四室乙丙组.V-Al催化体系催化-乙丙共聚合［J］，1978，1(1)，42- 49.
［3］　刘大华.乙丙橡胶［J］.合成橡胶工业手册，1991(1)，622-635.
［4］　USP，3 598 738.，1971-08-10.
［5］　BP，1 239 082.，1973-10-15.
［6］　杨明.乙丙聚合物粘度添加剂试生产［J］.合成橡胶工业，1992，15(1)，16-20.

收稿日期：2000-04-28