弹性体
CHINA ELASTOMERICS
2000　Vol.10　No.3　P.18-20

三元乙丙橡胶溶液接枝丙烯腈

张卫英　李晓　李新宇　李贺

　　摘要：对三元乙丙橡胶在二甲苯中与丙烯 腈的接枝共聚进行了研究，结果表明AIBN可以 有效引发接枝共聚，并且正交实验发现单体用量、引发剂浓度和反应温度均对接枝率有重 要影响，条件适当接枝率可达15%以上。实验证明，接枝共聚物对丁腈橡胶／三元乙丙橡胶 并用具有明显的增容作用。
　　关键词：三元乙丙橡胶；丙烯腈；接枝共聚；正交设计；并用 胶
　　中图分类号：TQ333.4；TQ316-343　　 文献标识码：A　　文章编号：1005-3174(2000)03-0018-03

Graft copolymerization of acrylonitrile onto EPDM in xylene

ZHANG Wei-ying,LI Xiao,LI Xing-Yu,LI He
（Department of Chemical Engineering,Fuzhou University,Fuzh ou　350002，China）

ABSTRACT

　　The graft copolymerization of acrylonitrile(AN) onto ethylene-propylen e-diene terpolymer(EPDM)in xylene was studied.Azobisisobutyronitrile(AIBN) was used as initiator and proved efficient to start grafting.The results of orthogon al experimentation showed that the concentration of monomer,initiator and reacti on time had important effects on the grafing degree.The grafting degree reached above 15% when the reaction conditions were controlled properly.The EPDM grafted with AN was shown efficient to improve NBR／EPDM blending compatibility.
　　Key words:EPDM;acrylonitrile;graft copolymerization;orthog onal design;rubber blend

作者简介：张卫英(1971-)，女，福建浦城人，硕士，在福州 大学化工系主要从事高分子材料的加工及应用改性研究，已发表学术论文数篇。
张卫英（福州大学化学工程系，福建福州　350002）
李晓（福州大学化学工程系，福建福州　350002）
李新宇（福州大学化学工程系，福建福州　350002）
李贺（福州大学化学工程系，福建福州　350002）

参考文献：
［1］　吴祥龙.并用橡胶的共硫化［J］.橡胶工业，1981，28(1)：1.
［2］　Coran A Y.Blends of Dissimilar rubbers-Cure-Rate Incompatibility［J］.Ru bber Chemistry and Technology,1988,61(2):281.
［3］　潘泳康，阮吉敏，周达飞.GMA熔融接枝EPDM的研究［J］.功能高分子学报，1997，1 0(2)：149.

收稿日期：2000-07-03