羧基丁腈胶粉／聚氯乙烯共混型热塑性弹性体的制备

张军　 蒋晓明　 杨红旭　

摘　要：采用羧基丁腈胶粉(CNBRP)与聚氯乙烯(PVC)高温机械共混，制备共混型热塑性弹性体。红外光谱分析表明，在与聚氯乙烯共混时，羧基丁腈胶粉的羧基基团之间发生反应。选择PVC-100，CNBRP-40及其它助剂，可以制备具有良好力学性能，耐油性、耐溶剂性的热塑性弹性体。扫描电镜显示CNBRP/PVC共混体系具有较好的相容性。
关键词：羧基丁腈胶粉；聚氯乙烯；共混物；热塑性弹性体；力学性能；相容性
分类号：TQ-333.7；TQ-325.3　文献标识码：A
文章编号：1005-3174(2001)02-0001-04

Preparation of thermoplastic elastomer from CNBRP／PVC blends

ZHANG Jun（College of Material Science and Engineering,Nanjing University of Chemical Technology,Nanjing,210009,China）　
JIANG Xiao-ming（College of Material Science and Engineering,Nanjing University of Chemical Technology,Nanjing,210009,China）　
YANG Hong-xu（College of Material Science and Engineering,Nanjing University of Chemical Technology,Nanjing,210009,China）　

Abstract：CNBRP and PVC were mechanically blended and prepared as a thermoplastic elastomer.The carboxyl group reaction in CNBRP was investigated by IR.With PVC 100,CNBRP?40 and other additives mixed,a thermoplastic elastomer of good mechanical properties,solvent-resistance and oil-resistance was prepared.The blender has better compatibility.
Keywords：CNBRP；PVC;blender；thermoplastic elastomer；mechanical property；compatibility

参考文献：

［1］Berta D A.Preparation of thermoplastic elastomers by dynamic curing of polyolefins and ethylene-propylene rubber[P].美国专利：US 4948840,1989.
［2］Choudhury N R，Bhowmick A K.Strength of thermoplastic elastomers from rubber-polyolefin blends[J].Journal of Materials Science,1990,25(1):161－167.
［3］张军，钱润男，秦志英，等.PVC／NBR再生胶共混型热塑性弹性体的研究[J].合成橡胶工业，1998，21(3)：168－171.
［4］邓本诚.橡胶并用与橡塑共混技术——性能、工艺与配方[M].北京：化学工业出版社，1998.
［5］张军.PVC／NBR并用非硫化型热塑性弹性体的研究[J].高分子材料科学与工程，1991.7(20)：115.
［6］De S.K.,Bhowmick A.K.Thermoplastic elastomers from rubber-plastic blends[M].Ellis Horwood Limited,1990.

收稿日期：2000年2月15日

出版日期：2001年4月1日